• Enhanced radiopacity:
• AH Plus offers increased radiopacity to ensure clear visibility, even in very thin layers formed during lateral condensation techniques. This improvement is achieved through advanced fillers with higher absorption capacity.
• Low shrinkage, minimal solubility, and controlled expansion:
• Designed to deliver a highly airtight seal, AH Plus minimizes shrinkage and solubility—key factors that determine the long-term impermeability and success of root canal fillings.
• Optimal film thickness:
• With a film thickness of just 26 µm, AH Plus stays well below the ISO requirement of < 50 µm for root canal sealers, ensuring reliable adaptation within the canal.
• Ideal flow characteristics:
• Its slightly thixotropic nature ensures smooth mixing and effortless insertion into the canal, while maintaining stability once placed. A flow rating of 36 mm exceeds ISO standards (> 25 mm).
• Superior sealing performance:
• AH Plus provides excellent sealing capabilities, effectively creating an impermeable barrier within the root canal.
• Strong adhesion to dentin:
• The sealer adheres securely to dentin, reducing the risk of microleakage and helping maintain a cohesive, long-lasting filling mass.

Dentsply AH Plus Root Canal Sealing Material is a two-component epoxy-amine resin–based paste system designed to provide a dependable seal within the root canal. Its extremely low shrinkage makes it a highly reliable option for achieving long-term impermeability. AH Plus is also well-suited for use with ProTaper Thermafil obturators, as its setting reaction remains stable and unaffected by thermoplastic obturation techniques.

Indications:

• Used alongside obturation materials to create an effective and lasting seal within the root canal system.

Advantages:

• Compatible with both hot and cold obturation techniques
• Provides a tight, durable seal
• Offers self-adhesive properties for improved retention
• Maintains dimensional stability after setting
• Highly biocompatible formulation
• Demonstrates moderate antimicrobial activity
• Extremely radiopaque, ensuring clear and reliable visibility on radiographs

Composition

• AH Plus Paste A:
• Bisphenol-A epoxy resin
• Bisphenol-F epoxy resin
• Calcium tungstate
• Zirconium oxide
• Silica
• Iron oxide pigments
• AH Plus Paste B:
• Dibenzyldiamine
• Aminoadamantane
• Tricyclodecane-diamine
• Calcium tungstate
• Zirconium oxide
• Silica
• Silicone oil

Caution:

• Do not interchange tube caps. The colored cap must remain with the colored tube, and the white cap with the white tube.

Working Time:

• Minimum of 4 hours at 23 °C.

Setting Time:

• Minimum of 8 hours at 37 °C.

• 1 x 4ml Paste A
• 1 x 4ml Paste B
• 1 X Mixing Pad

• Step 1: Root Canal Preparation
• Thoroughly prepare, clean, and dry the root canals before applying AH Plus.
• Use modern endodontic techniques to ensure optimal canal condition.
• Step 2: Dosage and Mixing
• For tube application, combine equal volumes (1:1) of Paste A and Paste B.
• Mix on a glass slab or mixing pad using a metal spatula.

Continue mixing until a smooth, homogeneous consistency is achieved.